Fixturing time 5 to 10 minute or slightly longer, depending on the size and configuration of the parts
Lap shearaluminum to aluminumCured at 75°Ffor 24 hours
700-800 psi
Lap shearaluminum to aluminumCured at 75°F for 8 hoursthen +250°F for 3 hours
2,300-2,500 psi
TENSILEMODULUS, 75°F
VolumeResistivity, 75°F
DielectricStrength, 75°F
TEMPERATURE RANGE
Fixturing time 5 to 10 minute or slightly longer, depending on the size and configuration of the parts
Color coded with Part A being white and Part B black
Non-critical 1:1 mix ratio by weight or volume
Smooth paste consistency
Can be mixed and cured at temperatures as low as 50-60°F, but with longer cure times
High bond strength to a wide variety of substrates