Product	Certifications	Applications	Viscosity	Cure Schedule	Hardness	Temp. Range	Link to Content
Supreme 46HT-2ND2 Non-drip, two component epoxy system for bonding, sealing and coating Tensile Lap Shear Strength 2,800-3,000 psi Tensile Modulus 350,000-400,000 psi	RoHS Compliant 1,000 Hours at 85°C/85% RH	Bonding Sealing Coating Gap Filling	paste	250-300°F for 3-4 hours, followed by a post cure at 350-400°F for 1-2 hours	80-90 Shore D	-100°F to +500°F	/fr/tds/supreme-46ht-2nd2
Supreme 46HTQ Two component epoxy system for bonding, sealing and casting Dielectric Constant 4.6 Tensile Lap Shear Strength 2,000-2,200 psi	RoHS Compliant	Bonding Sealing Casting Coating Gap Filling Encapsulation Potting	10,000-25,000 cps	4-6 hours at 250°F and 3-4 hours at 300°F	85-95 Shore D	-60°F to +450°F	/fr/tds/supreme-46htq
Supreme 62-1 Two component epoxy resin system featuring excellent temperature and chemical resistance Dielectric Constant 4.2 Tensile Lap Shear Strength 1,600-1,800 psi	NASA Low Outgassing RoHS Compliant	Bonding Sealing Coating Gap Filling	15,000-25,000 cps	Typical cure schedules range from 4-6 hours at 140-158°F [60-70°C], 20-40 minutes at 176-212°F [80-100°C] or 10-20 minutes at 257°F [125°C]	75-85 Shore D	-60°F to +450°F	/fr/tds/supreme-62-1
Supreme 70CN Two component, toughened epoxy system for bonding, sealing, coating and potting derived from natural substances Dielectric Constant 4.5 Volume Resistivity >10¹⁴ ohm-cm	RoHS Compliant NASA Low Outgassing	Bonding Sealing Coating Potting Encapsulation Gap Filling	8,000-12,000 cps	overnight at 75°F followed by 4-5 hours at 140-170°F	75-85 Shore D	-150°F to +400°F	/fr/tds/supreme-70cn
UV10 UV curable, very low viscosity adhesive, sealant and coating Dielectric Constant 3.5 Refractive Index 1.557	1,000 Hours at 85°C/85% RH RoHS Compliant	Bonding	250-500 cps	UV light at 325-365 nm for 20-30 seconds	70-80 Shore D	-60°F to +250°F	/fr/tds/uv10
UV10-FD UV curable, very low viscosity adhesive, sealant and coating; contains a flourescent dye for identification Refractive Index 1.557 Volume Resistivity >10¹⁴ ohm-cm	RoHS Compliant 1,000 Hours at 85°C/85% RH	Bonding	250-500 cps	UV light 325-365 nm for 20-30 seconds	70-80 Shore D	-60°F to +250°F	/fr/tds/uv10-fd
UV10LV UV curable, very low viscosity adhesive, sealant and coating Dielectric Constant 3.7 Refractive Index 1.557	RoHS Compliant	Bonding	150-350 cps	20-30 seconds when exposed to a UV light source emitting at a wavelength of 320-365 nm with an energy output as low as 20-40 milliwatts/cm2	70-80 Shore D	-60°F to +250°F	/fr/tds/uv10lv
UV10Med UV curable, biocompatible, low viscosity compound Refractive Index 1.557 Volume Resistivity >10¹⁴ ohm-cm	1,000 Hours at 85°C/85% RH ISO 10993-5 for Cytotoxicity RoHS Compliant USP Class VI Medical	Bonding	250-500 cps	20-30 seconds when exposed to a UV light source emitting at a wavelength of 320-365 nm with an energy output as low as 20-40 milliwatts per cm²	70-80 Shore D	-60°F to +250°F	/fr/tds/uv10med
UV10TK40M One component, higher viscosity UV curable system for bonding, sealing and coating Glass Transition Temperature (Tg) 135-140°C Refractive Index 1.55	1,000 Hours at 85°C/85% RH RoHS Compliant NASA Low Outgassing	Bonding Sealing Coating Encapsulation	30,000-60,000 cps	cures readily in 20-30 seconds when exposed to a UV light source emitting at a wavelength of 320-365 nm with 20-40 milliwatts per cm²	75-85 Shore D	-60°F to +450°F	/fr/tds/uv10tk40m
UV10TK40RCL Red colored UV curable epoxy acrylate system turns clear upon exposure to UV light Dielectric Constant 3.9 Refractive Index 1.55	RoHS Compliant 1,000 Hours at 85°C/85% RH	Bonding Sealing Coating Encapsulation	30,000-60,000 cps	UV light 325-365 nm for 30-90 seconds after the color change	75-85 Shore D	-60°F to +450°F	/fr/tds/uv10tk40rcl